High quality fine UD Carbon fabric 50 g/m² / 1.47 oz/yd² – Unidirectional fabric - sample. The material is thick, opaque and compact.
It is only an sample of the material, 20x50cm / 7.87“x19.68“
Unidirectional non crimp fabric, lying absolutely flat, almost 100 % utilisation of fibre properties, above all considerably higher compressive strength than fabric, higher fibre content possible, all cuts possible without fraying. Film on one side.
Calculated data for hand laminates with 45 volume percent fibres:
Resin consumption: 43.75 g/m², laminate thickness: 0.068 mm, laminate weight: 93.75 g/m²
Weaving style: Unidirectional, spread tow, with X-ply inbetween 2 very thin layers of carbon
Weft: No weft (warp fibers are held in place by chemical binder and very thin, non prominent X-ply net (4 g / sq.m.)
Material as per aircraft standards.
If you a interested you can also get sheet by your desired dimensions.
|
Specification: |
||
|
|
Nominal |
Tolerance: |
|
Fiber: |
UD Carbon fabric 50 g/m², 1.47 oz/yd² |
|
|
Fibre description |
ZOLTEK™ PX35 50k |
|
|
Weight: |
50 g/sqm || 1.47 oz/yd² |
± 5% |
|
Thickness: |
0.06 mm* |
|
|
Weave: |
Unidirectional, spread tow |
|
|
Width: |
50 cm |
|
|
Tensile strength (MPa): |
4137 |
|
|
Tensile modulus (GPa): |
242 |
|
|
Elongation at break (%): |
1.5 |
|
|
Warp – Weft ratio: |
||
|
|
Warp |
Weight Content (%) |
|
Fibre description: |
ZOLTEK™ PX35 50k |
86 |
|
Polyester fiber X ply |
4 g/m2 |
5 |
|
Adhesive, resin compatible |
7 g/m |
9 |
|
Yarn titer: |
50k |
|